Product Model | YQ-A1 | YQ-A2 | YQ-A3 | YQ-B1 | YQ-B2 | YQ-B3 | ||||||
Component | Black Ball Clay Ore(Raw Clay) | Raw White Clay | Refractory Clay | Black Ball Clay In Powder(For Refractory) | White Ball Clay In Powder(For Refactory) | Ball Clay In Powder(For Ceramic Board Production) | ||||||
Shape | Cake | Powder | Cake | Powder | Cake | Powder | Cake | Powder | Cake | Powder | Cake | Powder |
Moisture | 20% | 8% | 20% | 8% | 20% | 8% | 20% | 8% | 20% | 8% | 20% | 8% |
Mesh | 200 | 200 | 200 | 200 | 200 | 200 | ||||||
SiO2 | 56.10 | 53.97 | 33.02 | 61.85 | 54.60 | 57.93 | ||||||
Al2O3 | 25.04 | 29.81 | 48.24 | 26.15 | 33.40 | 27.83 | ||||||
CaO | 0.16 | 0.03 | 0.60 | 0.20 | 0.31 | 0.29 | ||||||
MgO | 0.43 | 0.25 | 0.45 | 0.19 | 0.21 | 0.27 | ||||||
Fe2O3 | 1.48 | 0.93 | 0.69 | 1.47 | 1.11 | 1.05 | ||||||
TiO2 | 0.74 | 1.98 | 1.57 | 0.45 | 0.53 | 0.47 | ||||||
K2O | 1.30 | 0.64 | 0.12 | 1.45 | 0.82 | 1.17 | ||||||
Na2O | 0.65 | 0.67 | 0.62 | 0.12 | 0.22 | 0.71 | ||||||
Loss | 13.20 | 10.15 | 14.55 | 8.02 | 8.80 | 7.80 | ||||||
Shrink | 7.60 | 12.40 | 7.90 | 6.70 | 10.60 | 5.00 | ||||||
1200℃ Firing Whiteness | 45.00 | 42.00 | 82.00 | 55.50 | 66.00 | 45.00 | ||||||
Strength of Green Body(kg) | 46.00 | 42.00 | 38.00 | 37.00 | 33.00 | 48.00 | ||||||
Water Absorption | 9.30 | 7.80 | 14.80 | 12.30 | 11.20 | 10.13 | ||||||
Viscosity | 49.00 | 45.00 | 51.00 | 48.00 | 44.00 | 51.00 | ||||||
Refractoriness (℃) | 1530℃ | 1370℃ | 1796℃ | 1614℃ | 1725℃ | - |